Intellige WELDING defectus facile - Laminar rimas

Welding rimas sunt maxime nocivis genus welding defectus, qui graviter afficit perficientur et salus et reliability de structuris. Hodie, ego te scire unus ex rimis - Saleed Cracks.

01

Non-metallicis inclusions, quidam non-metallicis inclusions (ut sulfides, silicates) in ferro volvitur in Steel ad Circumdurit in Differentias et principalis causa Laminar, inde in potentia et principalis causa Laminar, inde in potentia et principalis de Laminar in Structures et in potentia ad Malignum.

02

Refrenet accentus. Ob scelerisque cycle de welding, ibi erit in coercitionem vim in iuncturam. Nam datum advolvit crassitudine laminam T informibus et crucem iuncturam, sub conditione constanti welding parametri, ibi est a critica moderatur accentus vel flectendo. Vires, cum hoc maius hoc est facile producere Lamellar lactis.

03

Diffusio de hydrogenii, hydrogenii est promovens elementum pro elit. Ex diffusione hydrogenii et compositum moleculis, loci accentus crescit acriter. Cum autem hydrogenii accumulat ad finem inclusion, is promovet amissionem adhaesionem inter non-metallicis inclusion et metallum, et conteram adiacentibus inclusions. In metallum exhibet hydrogenii effecerunt fractura characteres fractura.

04

Base metallum proprietatibus, quamvis inclusions sunt pelagus causa lamellaris lacerationem, mechanica proprietatibus metallum etiam habent significant labefactum in lamellaris discerpens. In plastic lenta ad metallum est pauper, facilius est vox est ad expand, id est dicere, quod facultatem resistere Lamellar sciderit pauper est.

Ut ne eventum stratum rimas, Z directionem accentus et accentus concentration sunt maxime vitandum in consilio et constructione processus. Quod speciales sunt sicut sequitur:

I. emendare iuncturam consilio et reducere cohibere iactabantur. Imprimis mensuras superiores ut: extendens finem arcus ignitio laminam ad quandam longitudinem, quae est effectus prohibendi crack initiation; changing the welding seam layout to change the direction of the shrinkage stress of the welding seam, changing the vertical arc ignition plate to the horizontal arc ignition plate, changing the position of the weld, Making the total stress direction of the joint parallel to the rolling layer can greatly improve the resistance to laminar tearing. 

 II. Factum est utile adoptare idoneam modi, ut Gas tuta Welding et demergi arcus welding, cum humilis tendentia frigoris fregisset, quod est utile amplio resistentia ad Laminar. 

 3. Using low-strength matching welding materials, when the weld metal has a low yield point and high ductility, it is easy to concentrate the strain on the weld and reduce the strain in the heat-affected zone of the base metal, which can improve the resistance to laminar tearing. 

 IV. In application of welding technology, superficiem surfacing secum solitudinem layer adhibetur; Et Welding est commensus facere in iactabantur distribution et reducere in iactabantur concentration. 

 V. Ut ne laminarius lacerare fecit per frigus fregisset, quidam modos ne frigus fregisset, ut adoptari quantum fieri potest, ut oportet augmentum preheating, potestate et alias accentus relevium modi potest etiam adoptari. VI. Nos potest etiam control magnitudinem de welding et adopt et adoptius processus parva welding pedes et multi-saltum Welding.