Quid summus ipsum ferro est difficile ad weld

High-Carbon ferro refers to w (c) altior quam 0,6% of Carbon ferro, quod habet maius tendentia ad durare quam medium ipsum ferro, et formatio altus-Carboni martensite, magis sensitivo ad formationem frigus rimas.

In eodem tempore, Martensite organization formatae in aegre calor, affectus zonam, difficile et fragile proprietatibus, unde in a significant reductionem in plasticity et lenta est admodum pauperes, et ad specialem Welding processus ut ad perficientur ad specialem, ut ad perficientur de iuncturam.

Ideo in structuram soluta, plerumque raro usus est. Altus-Carbon ferro maxime propter apparatus partibus requirere princeps duritia et gerunt resistentia, ut sagittas, magna annus et coullings, etc.

Ut salvum Steel et simpliciorem machining processus, haec apparatus partes sunt etiam saepe combined in Structures. In gravibus apparatus vestibulum, Welding of High Carbon Steel components etiam offendit.

Dum developing in Welding processus summus ipsum ferro weldments, a comprehensive analysis de variis welding defectus, ut exsurgunt et correspondentes solutione processus mensuras superiores accipi.

I Weldability of High Carbon Steel

1.1 Welding modum

High-Carbon ferro maxime usus est summus duritiem et altum gerunt resistentia structurae, ita pelagus welding modi sunt electrode arcum welding, brazing et demergi arcum welding.

1.2 Welding Material

High-Carbon Steel Welding plerumque non eget in robore ad iuncturam et basi materia. Welding Electrode Arcus Welding est plerumque solebat removere sulphure capacitatem, humilis hydrogenii contentus de diffusione deposita metallum, bonum lugulae humilis-hydrogenii genus welding virga. In requisitis deficiente metallum et parentis materia et alia vires, correspondentes gradu humilis hydrogenii electrode debet esse; In aegre metallum et parens materia et alia vires, vires vires utendum est infra parens materia humilis-hydrogenii electrode meminisse non eligere vires gradu quam parens materia excelsum electrode. Si basis materia non liceat ad preheat cum Welding, ut ne frigus fregisset in calor, affectus zone, austenitic immaculatam ferro et fregisset virga potest ad obtinendum bonum plasticity et fregisset resistentia Austenzation Organization.

1,3 Bevel praeparatio

Ut limit Missam fractionem carbonis in Weld metallum, fusione Ratio reduci, ita communem usum u aut V informibus bevels cum Welding et operam ad Bovel et Bevels utrimque 20mm range olei et rubiginem et alias emundare.

Preheating 1,4

Structural Steel Electrode Welding, Welding debet preheated ante, preheating temperatus imperium ad CCL ℃ ~ CCCL ℃.

1.5 Interlayer Processing

Multi-accumsan multi-channel welding, primum Welding per parva diametri welding virga, parva current welding. Generally place the workpiece in a semi-standing welding or use the welding rod lateral swing, in order to make the entire heat-affected zone of the parent material are heated in a short period of time, in order to obtain preheating and insulation effect.

1.6 Post-Weld calor curatio

Statim post welding, in workpiece est positus in calefacit fornacem et tenuit DCL ° C accentus relevium annealing.

II summus ipsum Steel Welding defectus et Praecaventur mensuras superiores

Debitum ad summus ipsum ferro indurare tendentia valde magna, in welding prone ad calidum fregisset et frigus elit.

2.1 Praecaventur mensuras pro scelerisque fregisset

(I) imperium chemical compositionem de Weld, stricte imperium sulphuris et phosphoro contentus, et recte auget moles manganese ad amplio weld organization et redigendum segregationem.

II) Control figura de Weld section, latitudo-ut-altius ratio sit leviter maius vitare deviationem de weld centrum.

(III) ad rigidos partibus, eligendum oportet quodammodo parametri oportet, oportet quodammodo welding ordinem et directionem.

IV) Preheating et tardus refrigerationem mensuras superiores sunt, cum necessarium ne generationem scelerisque rimas.

(V) amplio alkalinity de electrode vel fluxum ad redigendum in immunditia contentus de weld et amplio gradum segregationis.

2,2 frigus fregisset praeventionis 

I) preheating ante welding et tardus refrigerationem post welding non solum reduces duritiam et fragtilitatem calor, affectus zonam, sed etiam accelerat externum diffusionem Hydrogenii in Weld.

II) Discriptis convenientem welding mensuras superiores.

III) capere convenit ecclesiam et welding sequence ad redigendum ad coactum accentus de iuncturam et amplio accentus statu de partibus.

IV) Select idoneam Welding materiae, siccam in Welding virga et fluxus ante welding, et faciam illud sicut vos.

V) Ante Welding, aquam, rubigo et alii lutum in basi metallum superficiem circa livorem debet esse diligenter remota ad redigendum contentus de hydrogenii in weld.

VI) hydrogenii curatio debet ferri ex statim ante welding, ut hydrogenii potest plene evadere a scanded iuncturam.

VII) Annealing curatio accentus relevium debet ferri ex statim post welding ad promovere diffusio hydrogenii in Weld foris